dc.contributor.authorRamalho, A.L.-
dc.contributor.authorAntunes, F.-
dc.contributor.authorNobre, Telmo-
dc.contributor.authorFerreira, J.A.M.-
dc.date.accessioned2019-02-08T16:31:28Z-
dc.date.available2019-02-08T16:31:28Z-
dc.date.issued2018-11-
dc.identifier.citationRAMALHO, A. L. [et al.] (2018) - Caraterização mecânica do aço S 355 a temperatura elevada. In Iberic Conference on Theoretical and Experimental Mechanics and Materials,1; National Congress on Experimental Mechanics,11, Porto, 4-7 November - Proceedings. [S.l.]: INEGI.FEUP .ISBN: 978-989-20-8771-9. p. 205-212.pt_PT
dc.identifier.isbn978-989-20-8771-9-
dc.identifier.urihttp://hdl.handle.net/10400.11/6387-
dc.description.abstractNo presente trabalho pretende-se efetuar a caracterização mecânica do aço S 355 AR, EN 10025-4, a alta temperatura. A avaliação rigorosa da variação da tensão de cedência, do módulo de Young, do módulo de encruamento, do calor específico e do coeficiente de dilatação térmica, com a temperatura é essêncial na simulação numérica da distorção e das tensões residuais induzidas por campos térmicos. Embora esta informação esteja disponível em alguns códigos estruturais, como o Eurocódigo 3 parte 1.2, ela não inclui o efeito da composição química e da microestrutura. O aço S 355 AR é um material bastante utilizado em estruturas soldadas, onde a avaliação de distorções e tensões residuais é um problema usual. A caracterização mecânica do aço S 355 AR, EN 10025-4, foi obtida através de ensaios de tração isotérmicos realizados a temperaturas até 600 °C, por Calorimetria Exploratória Diferencial (DSC) realizada até à temperatura de 950 °C e por Análise Termomecânica (TMA) conduzida até aos 1350 °C. Os resultados obtidos diferem significativamente dos valores apresentados na parte 1.2 do Eurocódigo 3, para um aço ferrítico genérico.pt_PT
dc.description.abstractABSTRACT: The present work aims to assess the mechanical characterization of S 355 AR steel, EN 10025-4, at high temperatures. The precise evaluation of the variation of yield stress, Young module, hardening module, specific heat and coefficient of thermal expansion, with the temperature is a key problem in numerical simulation of the distortion and the residual stresses induced by thermal fields. Although this information are available in some of the structural codes, like Eurocode 3 part 1.2, it does not include the effect of chemical composition and microstructure. The S 355 AR steel is a material commonly used in welded structures, where the evaluation of distortion and residual stresses is an usual issue. The mechanical characterization of the S 355 AR steel, EN 10025-4, were obtained by tensile tests conducted at temperatures up to 600 °C, by Differential Scanning Calorimetry (DSC) at temperatures up to 950 °C and by Thermomechanical analysis (TMA) conducted up to 1350 °C. The obtained results differ significantly from the values presented in Eurocode 3 part 1.2 for a general steel.pt_PT
dc.language.isoporpt_PT
dc.publisherINEGI/FEUPpt_PT
dc.rightsopenAccesspt_PT
dc.rights.urihttp://creativecommons.org/licenses/by-nd/4.0/pt_PT
dc.subjectPropriedades mecânicas de açospt_PT
dc.subjectAço S 355pt_PT
dc.subjectCaracterização mecânica a alta temperaturapt_PT
dc.subjectSteel propertiespt_PT
dc.subjectS 355 steelpt_PT
dc.subjectMechanical characterization,pt_PT
dc.subjectHigh temperaturept_PT
dc.titleCaraterização mecânica do aço S 355 a temperatura elevadapt_PT
dc.typeconferenceObjectpt_PT
dc.description.versioninfo:eu-repo/semantics/publishedVersionpt_PT
degois.publication.firstPage205pt_PT
degois.publication.lastPage212pt_PT
degois.publication.locationPortopt_PT
degois.publication.title1st Iberic Conference on Theoretical and Experimental Mechanics and Materials/11th National Congress on Experimental Mechanicspt_PT
dc.peerreviewedyespt_PT
Aparece nas colecções:ESTCB - Comunicações em encontros científicos e técnicos

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
ArtigoSF_TEMM2018_A.pdf1,09 MBAdobe PDFVer/Abrir


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.